Low Viscosity
Low resin viscosity refers to strong resin fluidity, making processing and construction more convenient
Product Categories
-25 resin is a pre-accelerated, long-gel time unsaturated polyester resin with low viscosity, good glass fiber wettability, fast curing and air-drying properties.
-25 resin is a pre-accelerated, long-gel time unsaturated polyester resin with low viscosity, good glass fiber wettability, fast curing and air-drying properties. It is suitable for RTM and vacuum infusion forming process, and is used to manufacture glass fiber reinforced plastic fishing boats, auto parts, fan hoods and waterproof boards and other products.
Low resin viscosity refers to strong resin fluidity, making processing and construction more convenient
The reaction rate of resin from liquid to solid is fast
After curing at room temperature, the surface of the resin does not touch
Properties of Liquid Resin
Item | Unit | Index | Test method |
Appearance | —— | Purple-red transparent liquid | GB/T 8237.4.1.1 |
Viscosity | 25℃, Pa.S | 0.14-0.18 | GB/T 7193.1 |
Acid Value | MgKOH/g | 28-34 | GB/T 2895 |
Gel Time | 25℃, min | 50.0-80.0 | GB/T 7193.6 |
Solids Content | % | 54-60 | GB/T 7193.3 |
Gel time: 55% methyl ethyl ketone peroxide: 1%
Performance of resin casting body (for reference only)
Item | Unit | Casting body measured data | Test method | FRP measured data | Test method |
Barco Hardness |
| 49 | GB3854-05 | —— | GB3854-05 |
Heat Distortion Temperature | ℃ | 78 | GB/T1634-04 | —— | —— |
Bending Strength | MPa | 128 | GB/T2570-95 | 400 | GB/T1449-05 |
Flexural Modulus | MPa | 4200 | GB/T2570-95 | 21000 | GB/T1449-05 |
Tensile Strength | MPa | 55 | GB/T2568-95 | 420 | GB/T1447-05 |
Tensile Modulus | MPa | 4200 | GB/T2568-95 | 21000 | GB/T1447-05 |
Elongation at Break | % | 1.8 | GB/T2568-95 | 2.3 | GB/T1447-05 |
Compressive Strength | MPa | —— | GB/T2569-95 | 210 | GB/T1448-05 |
Compression Modulus | MPa | —— | GB/T2569-95 | 16000 | GB/T1448-05 |
Remarks:
① The sample preparation method shall be implemented according to GB 8237-87.
② Curing system: curing agent 55% MEKPO: 1%
③ Post-curing treatment: 60℃×2 hours + 100℃×2 hours
④ Glass fiber content: 70±3%
 Auto Parts |  Fishing Boats |
Union Composites
Union focuses on the manufacturing of composite materials and is the designated distributor of Jushi Group, which can provide customers with composite products of stable quality. Union is committed to meeting diverse customer needs and can customize products.
Q: What is the Transportation and Storage of Unsaturated polyester resin?A: The transportation shall comply with the chapter V of the Regulations on Measures for the Administration of Road Transportation Safety of Dangerous Goods.
Store below 25℃, Avoid direct sunlight, fire and heat. With the compliance of all above, 3 months shelf life should be granted.
Q: How do you pack the resin?A: 220KG/DRUM, 1 IBC=1000KG
Pallet size: 1.12*1.12*1.03M
1*20GP=80drums, 4drums=1 pallet, total 20pallets
1*40HQ=108drums, 4drums=1 pallet, total 27pallets.
Q: Can we get samples?A: Yes, we can provide free sample for you (within 6kg).
Q: What is the delivery time?A: It takes one month from production to shipment.
Q: Whether the resin can be customizedA: Yes, we can produce according to your requirments.